The glass bottle treatment process is that after the glass bottle is annealed, the monostearate, polyethylene, oleic acid, silane, silicone or other polymer emulsion is sprayed into a mist, which is attached to the surface of the glass bottle with a certain temperature (the temperature of the bottle depends on the spraying material, about 21 ~ 80°C) to form a protective layer with wear resistance and lubrication.
Process glass bottle hot coating is carried out after bottle forming and before annealing treatment. When the process glass bottle is slowly cooled to 500 ~ 600℃, the metal coating agent is sprayed on the surface of the container to form a protective film of a certain thickness, which enhances the surface strength of about 30%, and can make the bottle withstand long-term water washing and washing.
Organic polysiloxane hydrophobic film and polymerization (Si02) can be formed by using silicone evaporation coating or impregnation with silicone on the glass surface. A silicon film connected to a glass surface by a common silicon bond. After heat treatment, the organic groups will be volatilized and the remaining silicon oxide film can be filled in the crack, and the hydrophobicity can avoid the diffusion of the active medium in the crack and the surface crack is healed, not only the strength and chemical stability of the glass are improved, but also the glass has special optical properties and impact resistance.